Sensing properties of assembled Bi2S3nanowire arrays
2015
Bismuth sulfide (Bi2S3) nanowires were grown in porous aluminium oxide template and a selective chemical etching was applied to transfer the nanowires to a solution. Well aligned nanowire arrays were assembled on pre-patterned silicon substrates employing dielectrophoresis. Electron beam lithography was used to connect aligned individual nanowires to the common macroelectrode. In order to evaluate the conductometric sensing performance of the Bi2S3 nanowires, current–voltage characteristics were measured at different relative humidity (RH) levels (5–80%) / argon medium. The response of the Bi2S3 nanowires depending of RH is found to be considerably different from those reported for other ty…
Application of electrochemical impedance for characterising arrays of Bi2S3 nanowires
2015
Abstract Electrochemical Impedance Spectroscopy (EIS) was used to characterise the electrical properties of bismuth sulphide (Bi2S3) nanowires (NWs) templated within anodic aluminium oxide (AAO) membranes. A specially engineered cell, with a nominal electrolyte volume of 0.1–0.2 ml, was used to hold and measure the electrochemical impedance of the fragile NW/AAO samples. An equivalent circuit model was developed to determine the filling density of nanowires within the porous templates. The EIS method can be utilised to probe the nanowire filling density in porous membranes over large sample areas, which is often unobtainable using electron microscopy and conductive atomic force microscopy t…